Double Side Graphite Coated Copper Foil for Battery Anode (20 m L x 200mm W x 90 um T), 1 Roll, - GCCu-R

Double Side Graphite Coated Copper Foil for Battery Anode (20 m L x 200mm W x 90 um T), 1 Roll, - GCCu-R

RM0.00 MYR
RM0.00 MYR
Skip to product information
Double Side Graphite Coated Copper Foil for Battery Anode (20 m L x 200mm W x 90 um T), 1 Roll, - GCCu-R
  • Double Side Graphite Coated Copper Foil for Battery Anode (20 m L x 200mm W x 90 um T), 1 Roll, - GCCu-R
  • Double Side Graphite Coated Copper Foil for Battery Anode (20 m L x 200mm W x 90 um T), 1 Roll, - GCCu-R
Double Side Graphite Coated Copper Foil for Battery Anode (20 m L x 200mm W x 90 um T), 1 Roll, - GCCu-R

Double Side Graphite Coated Copper Foil for Battery Anode (20 m L x 200mm W x 90 um T), 1 Roll, - GCCu-R

SKU: double-side-graphite-coated-copper-foil-for-battery-anode-20-m-l-x-200mm-w-x-11-um-t-1-roll-gccu-r

Price: RFQ

Description

 The graphite-coated copper foil in a roll can be used as anode for pouch cell testing. SPECIFICATIONS Graphite coating Coating Thickness:80 um +/- 5 um (double side coated) ( 40 micron on each side) Total Thickness: 90 um +/- 8 um Foil Thickness: 10 um +/- 3 um Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll Double sides material density: 12.6 mg/cm2 Compaction density: 1.4 g/cm3 Active Material Proportion in Powder: 93.2% (Binder: SBR+CMC (2.5% SBR, 1.8% CMC), conductive carbon" Super P, 2.5% ) Specific Capacity Specific Capacity: 330mAh/g (Areal Capacity: 3.79 mAh/cm2; Measured by IEC standard : 0.2C current, 4.2V -2.5V cut off. Half cell)

Graphite coating
  • Coating Thickness:80 um +/- 5 um (double side coated) ( 40 micron on each side)
  • Total Thickness: 90 um +/- 8 um
    Foil Thickness: 10 um +/- 3 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 12.6 mg/cm2
  • Compaction density: 1.4 g/cm3
  • Active Material Proportion in Powder: 93.2% (Binder: SBR+CMC (2.5% SBR, 1.8% CMC), conductive carbon" Super P, 2.5% )
Specific Capacity

Specific Capacity: 330mAh/g (Areal Capacity: 3.79 mAh/cm2; Measured by IEC standard : 0.2C current, 4.2V -2.5V cut off. Half cell)