Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

RM0.00 MYR
RM0.00 MYR
Skip to product information
Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP
  • Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP
Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

SKU: double-side-lifepo4-lfp-coated-aluminum-foil-for-battery-cathode-20-m-l-x-200mm-w-x-90-um-t-1-roll-cal-r-lfp

Price: RFQ

Description

 The graphite-coated copper foil in a roll can be used as anode for pouch cell testing. SPECIFICATIONS Graphite coating Coating Thickness: ~117.4 um (double side coated) Total Thickness: 133.4 um Foil Thickness: 16 um Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll Double sides material density: 27.0±0.4 mg/cm2 Compaction density: 2.3 g/cm3 Active Material Proportion in Powder: 95.4% (PVDF and Super P is 2% and 2.6%, respectively) Specific Capacity 150 mAh/g (Area Capacity: 3.864 mAh/cm2); 0.1 C; 2.5-3.7 V; Electrolyte: 1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC Charging and Discharging Curve for the First Cycle Rate Testing Cycling Test

Graphite coating
  • Coating Thickness: ~117.4 um (double side coated) 
  • Total Thickness: 133.4 um
    Foil Thickness: 16 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 27.0±0.4 mg/cm2
  • Compaction density: 2.3 g/cm3
  • Active Material Proportion in Powder: 95.4% (PVDF and Super P is 2% and 2.6%, respectively)
Specific Capacity

150 mAh/g (Area Capacity: 3.864 mAh/cm2); 0.1 C; 2.5-3.7 V; Electrolyte: 1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC

  • Charging and Discharging Curve for the First Cycle
  • Rate Testing
  • Cycling Test