Precursor Powder of NCMOH622 for High Capacity NCM Cathode Powder 200g/bottle - Lib-PNCM622

Name: Precursor Powder of NCMOH622 for High Capacity NCM Cathode Powder 200g/bottle - Lib-PNCM622
Brand: MTI
SKU: Lib-PNCM622
Availability: OutOfStock

SKU: precursor-powder-of-ncmoh622-for-high-capacity-ncm-cathode-powder-200g-bottle-lib-pncm622

Price: RFQ

Specifications

Lib-PNCM622 is the precursor powder of NCMOH622 for High Capacity NCM Cathode Powder at your own composition. There are 200 grams in one bottle Note: You must mix the precursor with LiOH. H2O and calcine the mixed powder at 750- 790oC before use Specification Package 200g/bottle in a vacuumed bag Composition NCMOH622 (Ni:Co:Mn = 6.503 : 1.569: 1.928) Configuration Sphere Particle size distribution D104.33 μm D509.89 μm D9018.22 μm Specific surface area 4.09 m^2/g Tap Density ≥1.64 g/cm^3 Water Content wt%0.36 PPH value ~ 8.05 Main Element Required Content (mol) Ratio (Ni:Co:Mn) Li 0 0 Ni 40.0528 6.503 Co 9.6601 1.569 Mn 11.8743 1.928 Impurity Requiredppm Typicalppm Ca 300 18 Cu 50 8 Fe 100 18 Mg 300 19 Na 500 232 Zn 100 102 SO4 5000 3300 Note MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery. If you need a larger quantity or have a question for IP, we will forward your inquiry to the producer. Application Notes : Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry . Please keep the powder in a vacuum box to avoid moisture. Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity. Related Products Vacuum Storage Box Powder Milling & Mixer Electrode Coaters Battery Research Equipment Other Battery Powder s Solid Electrolyte

Specification
Package	200g/bottle in a vacuumed bag
Composition	NCMOH622 (Ni:Co:Mn = 6.503 : 1.569: 1.928)
Configuration	Sphere
Particle size distribution	D104.33 μm D509.89 μm D9018.22 μm
Specific surface area	4.09 m^2/g
Tap Density	≥1.64 g/cm^3
Water Content	wt%0.36

PPH value	~ 8.05
	Main Element	Required Content (mol)	Ratio (Ni:Co:Mn)
	Li	0	0
	Ni	40.0528	6.503
	Co	9.6601	1.569
	Mn	11.8743	1.928
	Impurity	Requiredppm	Typicalppm
	Ca	300	18
	Cu	50	8
	Fe	100	18
	Mg	300	19
	Na	500	232
	Zn	100	102
	SO4	5000	3300
Note	MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery. If you need a larger quantity or have a question for IP, we will forward your inquiry to the producer.