Double-Side Coated LATP on PE Substrate Separator Roll as Flexible Solid-State Electrolyte (100 m L × 60 mm W × 16 um T) - Lib-2LATP-PE6016

Double-Side Coated LATP on PE Substrate Separator Roll as Flexible Solid-State Electrolyte (100 m L × 60 mm W × 16 um T) - Lib-2LATP-PE6016

RM0.00 MYR
RM0.00 MYR
Skip to product information
Double-Side Coated LATP on PE Substrate Separator Roll as Flexible Solid-State Electrolyte (100 m L × 60 mm W × 16 um T) - Lib-2LATP-PE6016
  • Double-Side Coated LATP on PE Substrate Separator Roll as Flexible Solid-State Electrolyte (100 m L × 60 mm W × 16 um T) - Lib-2LATP-PE6016
Double-Side Coated LATP on PE Substrate Separator Roll as Flexible Solid-State Electrolyte (100 m L × 60 mm W × 16 um T) - Lib-2LATP-PE6016

Double-Side Coated LATP on PE Substrate Separator Roll as Flexible Solid-State Electrolyte (100 m L × 60 mm W × 16 um T) - Lib-2LATP-PE6016

SKU: double-side-coated-latp-on-pe-substrate-separator-roll-as-flexible-solid-state-electrolyte-100-m-l-60-mm-w-16-um-t-lib-2latp-pe6016

Price: RFQ

Description

Double-Side Coated Li1.3 Al0.3 Ti1.7 (PO4)3 (LATP) on PE Substrate Separator Roll (100 m L × 60 mm W × 16 um T) that can be used as an excellent solid-state electrolyte separator for Li ion battery research. 

This flexible solid-state electrolyte roll can be used in our automatic stackers to prepare pouch cell and prismatic cell core.

Specifications

  • Material: Double-Side Coated Li1.3 Al0.3 Ti1.7 (PO4)3 (LATP) on Polyethylene (PE)
  • Thickness:                 16 um (12  um PE substrate and 2 um LATP on each side)
  • Width :                        60 ±0.5 mm
  • Length:                       100 m (customized length can be supplied upon request)
  • Air Permeability:        248 s/100mL
  • Porosity:                     42 %
  • Area Density:             13.0±1.0 g/m2
  • Puncture Strength :    ≥395 gf
  • Tensile Strength:        ≥ 1200 Kgf/cm2 (MD);   ≥1460 Kgf/cm2 (TD)
  • Thermal Shrinkage:    ≤2% (MD);   ≤1% (TD). Drying at 130℃ for 1 h. 
  • Sold in roll only