Double Side LiNiCoMnO2 (Ni:Co:Mn=6:2:2, NCM622) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM622

Double Side LiNiCoMnO2 (Ni:Co:Mn=6:2:2, NCM622) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM622

RM0.00 MYR
RM0.00 MYR
Skip to product information
Double Side LiNiCoMnO2 (Ni:Co:Mn=6:2:2, NCM622) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM622
  • Double Side LiNiCoMnO2 (Ni:Co:Mn=6:2:2, NCM622) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM622
Double Side LiNiCoMnO2 (Ni:Co:Mn=6:2:2, NCM622) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM622

Double Side LiNiCoMnO2 (Ni:Co:Mn=6:2:2, NCM622) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM622

SKU: double-side-linicomno2-ni-co-mn-6-2-2-ncm622-coated-aluminum-foil-for-battery-cathode-20-m-l-x-200mm-w-x-100-um-t-1-roll-cal-r-ncm622

Price: RFQ

Description

 The NCM622-coated aluminum foil in a roll can be used as cathode for pouch cell testing. SPECIFICATIONS NCM523 coating Coating Thickness: ~67 um (double side coated) Total Thickness: ~83 um Foil Thickness: ~15-16 um Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll Double sides material density: 22 ± 0.4 mg/cm2 Compaction density: 3.3 ± 0.1 g/cm3 Active Material Proportion in Powder: 97.5% (PVDF and Super P is 1% and 1.5%, respectively) Specific Capacity 170 mAh/g [0.1C, 3.0-4.3 V vs Li/Li+, Half Cell] [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]

NCM523 coating
  • Coating Thickness: ~67 um (double side coated) 
  • Total Thickness: ~83 um
    Foil Thickness: ~15-16 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 22 ± 0.4 mg/cm2
  • Compaction density: 3.3 ± 0.1 g/cm3
  • Active Material Proportion in Powder: 97.5% (PVDF and Super P is 1% and 1.5%, respectively) 
Specific Capacity

 

170 mAh/g [0.1C, 3.0-4.3 V vs Li/Li+, Half Cell] [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]